AluminaZC-M(α-βAlumina) Bricks - AZS Bricks Series





    1.Has a high resistance to acids, alkalis and glass liquids

    2.Used for contact with molten glass

    3.Used in the upper structure of glass melting furnaces

Description


ZC-M(α-βAlumina)Bricks - AZS Bricks Series Introduction

ZC-M(α-βAlumina) bricks for glass furnace is a white solid formed by pure alumina powder and zircon sand containing zirconia 65% and about 34% silica in the electric furnace and then injected into the mold to be cooled. The AZS bricks structure consists of an eutectoid and a glass phase of corundum and zirconium, AZS fused cast bricks are phased as eutectoids of the corundum phase and the zircon oblique phase, the glass phase is filled between their crystals.

ZC-M(α-βAlumina) Bricks - AZS Bricks Application

ZC-M(α-βAlumina) fire brick is formed by the compact structure of alpha-Al2O3 and beta-Al2o3 crystals. Refractory ZC-M(α-βAlumina) bricks have good corrosion resistance and stability, does’t contaminate molten glass.ZC-M(α-βAlumina) bricks are widely used in the parts such working end ,channels, feeders,and superstructure like melter.

ZC-M(α-βAlumina) Bricks - AZS Bricks Specification
 
Al203 94%
Na20 4%
alpha alimina 45%
beta alumina 53%
Vitreous Phase 2%
Cold Crushing Strength 200Mpa
Apparent porosity 2%
RefractorinessUnder Load of 0.2Mpa 1700℃
Exudation Temp 1400℃
Static corrosion of molten glass 0.3mm/24h

ZC-M(α-βAlumina) Bricks - AZS Bricks Using Precautions in Glass Kiln

1.Irregular Changes in Thermal Expansion

The expansion curve of the aluminaZC-M(α-βAlumina)refractory brick has an anomaly near 1000 °C, the internal ZrO2 crystal undergoes a reversible crystal transformation with a large volume change. Therefore, AZS bricks product containing ZrO2 should not be used at around 1000 °C, and the temperature of AZS refractory brick is often A region that fluctuates sharply. When baking the kiln, the temperature change at 900~1150 °C should not be too large, generally can not exceed 15 °C / h, requiring a steady temperature rise. fused cast AZS bricks parts should be protected from blowing cold air and protected by other bricks to prevent cracking.

2.Shrinkage

When casting, there are often shrinkage holes in the casting mouth, AZS refractory brick for the glass furnace body has more pores and poor density. Therefore, when the glass wall of the glass melting part is made, the shrinkage holes are directed toward the direction of the kiln. When AZS refractory brick is eroded to a very thin level, azs brick will cause a leakage of glass liquid. When used in the upper flame space of the kiln, the service life is very long, and there is no problem of running glass. Therefore, the casting port is used outwards to extend the service life.

3.Eutectic

The AZS refractory brick and the clay brick are in contact with the clay brick. The eutectic phenomenon occurs at a high temperature of 1300 °C. Therefore, when the refractory material is selected, the two refractory materials with severe eutectic phenomena should be avoided from contact with the masonry, such as silica brick casting. Below AZS fused cast bricks ,AZS brick is most susceptible to erosion by the fused cast AZS brick.

ZC-M(α-βAlumina) Bricks - AZS Bricks Packing & Delivery

Consider various and complex transportation conditions,fused cast AZS bricks products are packing following the highest standards with foam boards between every two blocks, corners protected with triangular hard card boards & multi-strengthened by steel bands and wrapping in plastic film on the outside.

For easy location of different materials,refractory aluminaZC-M(α-βAlumina) bricks for the glass furnace packing lists are places both inside and outside packages, shipping marks are clearly painted on all cases.

 