Mullite Refractory Brick Introduction
Mullite Bricks are an excellent quality high alumina refractory product with about 65~75 percent alumina content. Mullite brick is made of mullite as the main raw material and molded through high temperature firing and pressure. Mullite bricks have advantage performance on furnace and kiln application such as high temperature resistance, chemical and mechanical corrosion, good thermal shock resistance and so on.
Application of Mullite Brick
Mullite bricks are mainly used for top of hot blast stove, stack and bottom of blast furnace, regenerative chamber of glass melter, ceramic post sintering kiln, furnace lining for dead angle of petroleum cracking and etc.
Mullite Brick Technical Data
| Mullite Bricks | |||||
| Item | MU 60 | MU 65 | MU 70 | MU 75 | |
| Chemical Composition |
Al2O3 | ≥60 | ≥65 | ≥70 | ≥75 |
| SiO2 | ≤35 | ≤33 | ≤26 | ≤24 | |
| Fe2O3 | ≤1.0 | ≤1.0 | ≤0.6 | ≤0.4 | |
| Bulk Density g/cm3 | ≥2.55 | ≥2.55 | ≥2.55 | ≥2.55 | |
| Permanent Linear Change On Reheating (%) 1500℃X2h | 0~+0.4 | 0~+0.4 | 0~+0.4 | 0~+0.4 | |
| Apparent Porosity % | ≤17 | ≤17 | ≤17 | ≤18 | |
| Thermal Conductivity (W/MK) 1000℃ | 1.74 | 1.84 | 1.95 | 1.95 | |
| Cold Crushing Strength Mpa | ≥60 | ≥60 | ≥80 | ≥80 | |
| 20－1000℃ Thermal Expansich10-6/℃ | 0.6 | 0.6 | 0.6 | 0.55 | |
| 0.2Mpa Refractoriness Under Load T0.6 ℃ | ≥1580 | ≥1600 | ≥1600 | ≥1650 | |
| Thermal Shock Resistances 100℃ water cycles | ≥18 | ≥18 | ≥18 | ≥18 | |